PowerPoint プレゼンテーション

バインダ規格に関する調査
林信也
大谷正雄
焼山明生
CENのバインダ規格
Bituminous Binders
Paving Applications
Industrial Applications
Paving
Grade
Bitumens
Polymer
Modified
Bitumens
Cutback &
Fluxed
Bitumens
Cationic
Bitumen
Emulsions
Oxidised
Bitumens
Hard Grade
Industrial
Bitumens
EN 12591
EN 14023
prEN 15322
EN 13808
EN 13304
EN 13305
Hard
Paving
Grade
Bitumens
prEN 13924
EN12591：Bitumen and bituminous binders－Specification for paving
grade bitumens （ストアス）
舗装用アスファルトの針入度20×0.1㎜ to 330×0.1㎜の性状（1）
Unit
Penetration at 25℃
Test method
×0.1mm EN 1426
Grade designation
20/30
30/45
35/50
40/60
50/70
20-30
30-45
35-50
40-60
50-70
55-63
52-60
50-58
48-56
46-54
0.5
0.5
0.5
0.5
0.5
55
53
53
50
50
℃
EN 1427
-change of mass, maximum,±
%
EN 12607-1 or
EN 12607-3
-retained penetration, minimum
%
-softening point after hardening,
minimum
℃
EN 1427
57
54
52
49
48
Flash point, minimum
℃
EN 22592(b)
240
240
240
230
230
Solubility, minimum
%(m/m)
EN 12592
99.0
99.0
99.0
99.0
99.0
Softening point
Resistance to hardening, at 163℃(a)
(a)
(b)
Only RTFOT to be used for referee purposes
See 4.1.1.3
EN12591：Bitumen and bituminous binders－Specification for paving
grade bitumens （ストアス）
舗装用アスファルトの針入度20×0.1㎜ to 330×0.1㎜の性状（2）
Unit
Penetration at 25℃
Test method
×0.1mm EN 1426
Grade designation
70/100
100/150
160/220
250/330
70-100
100-150
160-220
250-330
43-51
39-47
35-43
30-38
0.8
0.8
1.0
1.0
46
43
37
35
℃
EN 1427
-change of mass, maximum,±
%
EN 12607-1 or
EN 12607-3
-retained penetration, minimum
%
-softening point after hardening,
minimum
℃
EN 1427
45
41
37
32
Flash point, minimum
℃
EN 22592(b)
230
230
220
220
Solubility, minimum
%(m/m)
EN 12592
99.0
99.0
99.0
99.0
Softening point
Resistance to hardening, at 163℃(a)
(a)
(b)
Only RTFOT to be used for referee purposes
See 4.1.1.3
EN12591：Bitumen and bituminous binders－Specification for paving
grade bitumens （ストアス）
舗装用アスファルトの針入度250×0.1mm to 900×0.1mmの性状
Unit
Penetration at 15℃
Dynamic viscosity at 60℃,
minimum
Kinematic viscosity at 135℃,
minimum
Pa-s
mm2/s
%
Grade designation
250/330
330/430
500/650
650/900
70-130
90-170
140-260
180-360
EN 12596
18
12
7.0
4.5
EN 12595
100
85
65
50
EN 12607-1
or
EN 12607-3
1.0
1.0
1.5
1.5
4.0
4.0
4.0
4.0
×0.1mm EN 1426
Resistance to hardening at
163℃(a)
-change of mass, maximum, ±
Test method:
-viscosity ratio at 60℃,
maximum
Flash point, minimum
℃
EN 22719
180
180
180
180
Solubility, minimum
%(m/m)
EN 12592
99.0
99.0
99.0
99.0
(a)
Only RTFOT to be used for referee purposes
EN12591：Bitumen and bituminous binders－Specification for paving
grade bitumens （ストアス）
柔らかいアスファルトのグレードおよび60℃における粘度
Unit
Test method
Grade designation
V1500
V3000
V6000
V12000
mm2/s
EN 12595
10002000
20004000
40008000
80001600
Flash point, minimum
℃
EN 22719
160
160
180
180
Solubility, minimum
%(m/m)
EN 12592
99.0
99.0
99.0
99.0
2.0
1.7
1.4
1.0
3.0
3.0
2.5
2.0
Kinematic viscosity at 60℃
Resistance to hardening, TFOT
120℃:
-change of mass, maximum, ±
-viscosity ratio at 60℃,
maximum
EN 12607-2
%
EN 14023：改質アスファルトについて
ポリマー改質アスファルトの基本となる性状およびグレード(1)
ESSENTIAL
REQUIREMENT
CHARACTERISTIC
TEST
METHOD
UNIT
Class for the essential requirements of polymer modified bitumens
0a
1b
2
3
4
5
Consistency at Intermediate
ServiceTemperature
Penetration at 25℃
EN 1426
0.1mm
TBR
10-40
25-55
45-80
40-100
Consistency at Elevated
Service Temperature
Softening Point
EN 1427
℃
TBR
≧80
≧75
≧70
≧65
Cohesionc
Force ductilityc
(Low speed traction) or
EN 13589
followed by
EN 13703
J/cm2
NPD
TBR
≧3
at 5℃
≧2
at 5℃
≧1
at 5℃
≧2
at 0℃
Tensile test at 5℃c
(High speed traction) or
EN 13587
followed by
EN 13703
J/cm2
NPD
TBR
≧3
≧2
≧1
-
Vialit pendulumc
(Impact test)
EN 13588
J/cm2
NPD
TBR
≧0.7
-
-
-
Change of mass
EN 12607-1
EN 12607-3
%
NPD
TBR
≦0.3
≦0.5
≦0.8
≦1.0
Retained Penetration
EN 1426
%
NPD
TBR
≧35
≧40
≧45
≧50
Increase in Softening Point
EN 1427
℃
NPD
TBR
≦8
≦10
≦12
-
Flas Pointe
EN ISO 2592
℃
≧250
≧235
≧220
-
Durabilityd
(Resistance to hardening,
EN 12607-1 or –3)
Other characteristics
a As the grading system is based on the consistency at intermediate and elevated service temperatures, values shall be given for these characteristics.
b Class 1 TBR shall not be used for regulatory declaration and marking purposes.
c One cohesion method shall be chosen based on end application.
Vialit cohesion (EN 13588) shall only be used for surface dressing binders.
d Resistance to hardening: for referee purposes, only RTFOT (see EN 12607-1) shall be used.
See 5.1.5. Resistance to hardening is not appropriate for surface dressing bitumens.
e For safety reasons, classes 0 and 1 shall not be used for flash point.
EN 14023：改質アスファルトについて
ポリマー改質アスファルトの基本となる性状およびグレード(2)
ESSENTIAL
REQUIREMENT
CHARACTERISTIC
TEST
METHOD
UNIT
Class for the essential requirements of polymer modified bitumens
6
7
8
9
10
Consistency at Intermediate
ServiceTemperature
Penetration at 25℃
EN 1426
0.1mm
65-105
75-130
90-150
120-200
200-300
Consistency at Elevated
Service Temperature
Softening Point
EN 1427
℃
≧60
≧55
≧50
≧45
≧40
Cohesionc
Force ductilityc
(Low speed traction) or
EN 13589
followed by
EN 13703
J/cm2
≧2
at 10℃
-
-
-
-
Tensile test at 5℃c
(High speed traction) or
EN 13587
followed by
EN 13703
J/cm2
-
-
-
-
-
Vialit pendulumc
(Impact test)
EN 13588
J/cm2
-
-
-
-
-
Change of mass
EN 12607-1
EN 12607-3
%
-
-
-
-
-
Retained Penetration
EN 1426
%
≧55
≧60
-
-
-
Increase in Softening Point
EN 1427
℃
-
-
-
-
-
Flas Pointe
EN ISO 2592
℃
-
-
-
-
-
Durabilityd
(Resistance to hardening,
EN 12607-1 or –3)
Other characteristics
a As the grading system is based on the consistency at intermediate and elevated service temperatures, values shall be given for these characteristics.
b Class 1 TBR shall not be used for regulatory declaration and marking purposes.
c One cohesion method shall be chosen based on end application.
Vialit cohesion (EN 13588) shall only be used for surface dressing binders.
d Resistance to hardening: for referee purposes, only RTFOT (see EN 12607-1) shall be used.
See 5.1.5. Resistance to hardening is not appropriate for surface dressing bitumens.
e For safety reasons, classes 0 and 1 shall not be used for flash point.
EN 14023：改質アスファルトについて
ポリマー改質アスファルトの基本となる性状およびグレード
TECHNICAL
REQUIREMENT
TEST
METHOD
Class for the technical requirements of polymer modified bitumens
UNIT
0
1a
2
3
4
5
6
7
8
9
10
Fraass Breaking Point
EN 12593
℃
NPD
TBR
≦0
≦-5
≦-7
≦-10
≦-12
≦-15
≦-18
≦-20
≦-22
Elastic recovery at 25℃
EN 13398
%
NPD
TBR
≧80
≧70
≧60
≧50
-
-
-
-
-
Elastic recovery at 10℃
EN 13398
%
NPD
TBR
≧75
≧50
-
-
-
-
-
-
-
Plasticity range
Sub-clause
5.1.9
℃
NPD
TBR
≧85
≧80
≧75
≧70
≧65
≧60
-
-
-
Storage stabilityb
Difference in softening point
EN 13399
EN 1427
℃
NPD
TBR
≦5
-
-
-
-
-
-
-
-
Storage stabilityb
Difference in penetration
EN 13399
EN 1426
0.1mm
NPD
TBR
≦9
≦13
≦19
≦26
-
-
-
-
-
Drop in softening point after
EN 12607-1 or –3
EN 1427
℃
NPD
TBR
≦2
≦5
-
-
-
-
-
-
-
Elastic recovery at 25℃ after
EN 12607-1 or –3
EN 13398
%
NPD
TBR
≧70
≧60
≧50
-
-
-
-
-
-
Elastic recovery at 10℃ after
EN 12607-1 or -3
EN 13398
%
NPD
TBR
≧50
-
-
-
-
-
-
-
-
NOTE
The following data may be given by the supplier of the polymer modified bitumen in the product data sheet:
-polymer dispersion (see EN 13632 [5]);
-solubility (see EN 12592 [4] using the appropriate solvent declared by the supplier);
-handling temperatures;
-minimum storage and pumping temperatures;
-maximum and minimum mixing temperatures; for comparison purposes, EN 13702-1 or EN 13702-2 should be used;
-density (see EN ISO 3838).
a Class 1 TBR shall not be used for regulatory declaration and marking purposes.
b If no data is given on the storage stability test (see EN 13399), information shall be given by the supplier regarding storage conditions for the polymer modified bitumen
to avoid separation of the components.
ASTMのバインダ規格
番号
D 946-82
D 5976-00
D 5840-00
D 5841-00
D 5892-00
D 6114-97
タイトル
S tandard S pecification for P enetoration-G raded
A sphalt C em ent for U se in P avem ent C onstruction
要約
舗装用ストレートアスファルト規格
道路建設に使用される針入度区分アスファルトセメ
ントの標準仕様
S tandard S pecification for TypeⅠ P olym er M odified この仕様は、道路建設に使用される特殊な添加剤を用いて改質されたアスファルトセメントを網羅しているも
A sphalt C em ent for U se in P avem ent C onstruction のである。これらは、ポリマー改質アスファルトを限定し利用可能な流通商品を参照するための規定として
工業化された。しかし、パフォーマンス‐ベースの仕様は意図されていなかった。よって、この仕様は、有効
道路建設に使用される改質アスファルトⅠ型の標準性が欠如しているとの判断により2005年7月に削除した。
仕様
改質材：SB S
S tandard S pecification for TypeⅡ P olym er M odified この仕様は、道路建設に使用される特殊な添加剤を用いて改質されたアスファルトセメントを網羅しているも
A sphalt C em ent for U se in P avem ent C onstruction のである。これらは、ポリマー改質アスファルトを限定し利用可能な流通商品を参照するための規定として
工業化された。しかし、パフォーマンス‐ベースの仕様は意図されていなかった。よって、この仕様は、有効
道路建設に使用される改質アスファルトⅡ型の標準性が欠如しているとの判断により2005年7月に削除した。
仕様
改質材：SB R ラテックス・クロロプレンラテックス
S tandard S pecification for TypeⅢ P olym er M odified この仕様は、道路建設に使用される特殊な添加剤を用いて改質されたアスファルトセメントを網羅しているも
A sphalt C em ent for U se in P avem ent C onstruction のである。これらは、ポリマー改質アスファルトを限定し利用可能な流通商品を参照するための規定として
工業化された。しかし、パフォーマンス‐ベースの仕様は意図されていなかった。よって、この仕様は、有効
道路建設に使用される改質アスファルトⅢ型の標準性が欠如しているとの判断により2005年7月に削除した。
仕様
改質材：EV A
S tandard S pecification for TypeⅣ P olym er M odified この仕様は、道路建設に使用される特殊な添加剤を用いて改質されたアスファルトセメントを網羅しているも
A sphalt C em ent for U se in P avem ent C onstruction のである。これらは、ポリマー改質アスファルトを限定し利用可能な流通商品を参照するための規定として
工業化された。しかし、パフォーマンス‐ベースの仕様は意図されていなかった。よって、この仕様は、有効
道路建設に使用される改質アスファルトⅣ型の標準性が欠如しているとの判断により2005年7月に削除した。
仕様
改質材：未加硫SB R
この仕様は、リサイクル利用の目的で廃タイヤゴムや必要に応じた添加剤を加え混合したアスファルトラ
S tandard S pecification for A sphalt-R ubber B inder バーを道路建設用に使用するためのものである。アスファルトラバーは、十分に熱いアスファルトを用いるこ
とと混合することによる相互作用によってゴム粒子の膨張を引き起こさせている。
アスファルトラバーバインダーの標準仕様
この仕様は、化学的なゲル化剤を用いて改質したアスファルトセメントの基準を網羅しているものである。化
学的に改質されたアスファルトを適用する場合の規準ならびに参照を示すために制定されたものである。試
験は、改質度合いを測定することが目的であり、性能について示すものではない。よって、性能基準として
D 6154-97
道路建設に使用される化学的な改質を施されたアスの仕様を意図するものではない。
ファルトの標準仕様
この仕様は、トリダッドレイクアスファルトを用いた改質アスファルトの基準を網羅しているものである。グ
S tandard S pecification for G raded Trinidad Lake
レード分類は平均 7 日最大の舗道設計温度、及び、最小の舗道設計温度に基づき行っている。
M odified A sphalt B inder
D 6626-01
トリニダッドレイクアスファルトにより改質されたアス
ファルトの標準仕様
S tandard S pecification for C hem ically M odified
A sphalt C em ent for U se in P avem ent C onstruction
ASTM D946：ストレートアスファルト
40-50
針入度
60-70
85-100
120-150
min
max
min
max
min
max
min
max
40
50
60
80
85
100
120
150
引火点
°F
450
－
450
－
450
－
425
－
伸度（25℃）
cm
100
－
100
－
100
－
100
－
99.0
－
99.0
－
99.0
－
99.0
－
55+
－
52+
－
47+
－
42+
－
トルエン可溶分
TFOT後の針入度残留率
TFOT 後の伸度（25℃）
％
％
cm
50
75
100
化学改質アスファルトおよびアスファルトラバーの規格
SHRPバインダ評価
出荷時の性状
施工直後の性状
長期供用後の性状
オリジナル
RTFOT
PAV
アスファルト
アスファルト
アスファルト
引火点
≧２３０℃
（安全性）
高温粘度
@135℃
≧２３０℃
（作業性）
質量損失率
≦1.00%
（熱劣化）
DSR
G*sinδ≦5.0MPa
（疲労クラック）
DSR
BBR
G*/sinδ≧2.2KPa
S≦300MPa ｍ≧0.3
（初期わだち掘
れ）
（低温クラック）
DSR
ＤＴＴ
G*/sinδ≧1.0KPa
破断ひずみ≧1.0%
（品質管
理）
（低温クラック）
パフォーマンスグレード
PG52
ﾊﾟﾌｫｰﾏﾝｽｸﾞﾚｰﾄﾞ（PG）
7日間平均最高舗装体温度
最低舗装供用温度（℃）
PG58
PG64
PG70
-10 -16 -22 -28 -34 -40 -46 -16 -22 -28 -34 -40 -16 -22 -28 -34 -40 -10 -16 -22 -28
<52
<58
<64
<70
ｵﾘｼﾞﾅﾙｱｽﾌｧﾙﾄ
ﾀﾞｲﾅﾐｯｸｼｪｱｰ
G*/Sinδ≧1.0KPa
52
58
64
70
52
58
64
70
RTFOT　ｱｽﾌｧﾙﾄ
ﾀﾞｲﾅﾐｯｸｼｪｱｰ
G*/Sinδ≧2.2KPa
PAV　ｱｽﾌｧﾙﾄ
ﾀﾞｲﾅﾐｯｸｼｪｱｰ
G*Sinδ≦5,000KPa
ｸﾘｰﾌﾟｽﾃｨﾌﾈｽ
S値　≦　300,000KPa
25 22 19 16 13 10
0
7
25 22 19 16 13 28 25 22 19 16 34 31 28 25
-6 -12 -18 -24 -30 -36 -6 -12 -18 -24 -30 -6 -12 -18 -24 -30
0
-6 -12 -18
m値　≧　0.30
供用中に発生する問題（わだち掘れ、疲労クラック、低温クラック）を考慮した
規格となっており、パフォーマンスグレード（PG)と呼ばれている。
PG○－□と表記する。（○は供用最高温度を示し、□は供用最低温度を示
す）
出展：SHRP－A－410（1994）
韓国のバインダ規格
KS F 2389