Part Number: EMS-0552821-060 Revision 20140225 - Generated 12-Mar-2014 Core Loss (mW/cm³) 10,000 Core Loss vs. Bpk - Super-MSS™ Sendust 60µ 500 kHz 250 kHz 100 kHz 50 kHz 25 kHz 10 kHz 5 kHz 1 kHz 400 Hz 60 Hz 1,000 100 10 10 100 1,000 Bpk - Peak AC Flux Density (gauss) 120 %Initial Perm vs. DC Bias - Super-MSS™ Sendust 60µ Nominal 110 10,000 Minimum Core Loss DC Saturation Coating/Pkg 1 a b H c Wire Size Full Winding AWG mm Turns Rdc(Ω) H 50 40 0 .4 N I Le H = DC Magnetizing Force (Oe) N = Number of Turns I = DC Current (A) Le = Effective Path Length (cm) 30 20 10 100 H - DC Magnetizing Force (Oe) Effective AL Value vs. DC Bias - EMS-0552821-060 200 150 100 50 0 0 500 10,000 d None N/A 10 2.500 31 11.8 m 1,000 NI (ampere turns) 1,500 2,000 Ampere Turns vs. DC Energy Storage - EMS-0552821-060 1,000 100 10 10 N/A 96 Halves/Box 8 3.150 20 4.8 m 1,000 250 where H expressed in oersteds, and: a=0.01, b=4.47E-06, c=1.74, d=0.00 HDC 100 Oe Percent Initial Perm(nom.) 42.2% Percent Initial Perm(min.) 34.7% Limit Package Quantity 60 1 f d Bpk 2 f 2 a b c 3 2 .3 1.65 Bpk Bpk Bpk Coating Type: Voltage Breakdown (min.) 70 0 where B pk expressed in gauss, f expressed in hertz, and: a=1.00E+06, b=9.97E+08, c=1.40E+07, d=1.92E-14 Bpk 1000 G frequency 50 kHz Core Loss (nominal) 225 mW/cm³ Core Loss (maximum) 259 mW/cm³ %µi = 80 10 WA - Min. Eff. Window Area 3.77 cm² sa - Surface Area 121 cm² mlt - mean length per turn 11.6 cm μi(reference) 60 AL value (nominal) 219 nH/N² Test Winding N=100, #16 AWG Frequency 10 kHz Voltage on Agilent 4284A 1.6 V AL tolerance ±8% Core Loss(mW/cm³)= Winding Table 2.161 ± 0.032 in 1.087 ± 0.016 in 0.811 ± 0.016 in 0.728 in (min.) 1.476 in (min.) 0.661 ± 0.013 in 120 grams/half 3.50 cm² 12.3 cm 43.1 cm³ 90 AL Value (nH/N²) 54.9 ± 0.81 mm 27.6 ± 0.41 mm 20.6 ± 0.41 mm 18.5 mm (min.) 37.5 mm (min.) 16.8 ± 0.33 mm (approximate) Ae - Eff. Mag. Cross Section Le - Eff. Mag. Path Length Ve - Eff. Core Volume NI (ampere turns) Inductance Magnetic Dimensions A B C D E F Mass % Initial Permeability (%µi) 100 12 2.000 49 29.6 m 14 1.600 75 72.1 m 16 18 1.250 1.000 117 180 178.8 m 437.6 m 100 1,000 10,000 DC Energy Storage ½LI² (µJ) 20 0.800 279 1.1 22 0.630 432 2.7 24 0.500 669 6.5 100,000 26 0.400 1,036 16.1 Micrometals Arnold Powder Cores, A Division of Micrometals, Inc. - 5615 E. La Palma Ave., Anaheim, California 92807 USA Ph: +1-714-970-9400, Toll Free in USA: +1-800-356-5977, Asia Pacific Sales: +852 3106 3736 www.MicrometalsArnoldPowderCores.com 1,000,000 28 0.315 1,603 39.6
© Copyright 2024 ExpyDoc